PA66-Compounds-TECACOMP-PA66-CF40-black
PA66-Compounds-TECACOMP-PA66-CF40-black

TECACOMP PA66 CF40 black 1014832

Nylon 66 reinforced with 40 % carbon fibers

PA 66 is a polyamide with great hardness, stiffness, abrasion resistance and heat resistance. Compounding with 40 % carbon fibers significantly enhances the good mechanical properties, and also increases electrical conductivity.  

TECACOMP PA66 CF40 black offers high specific strength at low density, which is particularly appreciated in automotive and mechanical engineering and electrical engineering. The composite can be used permanently up to 110 °C, and for short periods up to 170 °C.

Facts

Chemical designation
PA 66 (Polyamide 66)
Colour
black
Density
1.32 g/cm3

Main Features

  • very high stiffness
  • good wear properties
  • good heat deflection temperature
  • resistant to many oils, greases and fuels
  • good weldable and bondable
  • low viscosity

Downloads

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 262 MPa DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)
    26800 MPa DIN EN ISO 527-1
    Elongation at break (tensile test) 1,8 % DIN EN ISO 527-1
    Impact strength (Charpy) 47 kJ/m2 DIN EN ISO 179-1eU
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 5 - 72 C -
    Melting temperature 260 C -
    Heat distortion temperature 255 C ISO-R 75 Method A
    Service temperature 170 C short term -
    Service temperature 110 C long term -
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    volume resistivity 10-1 Ω*m DIN EN ISO 3915
  • product-technical-detail-collapse-item-3-lvl-1
    Processing parameter Value Unit Parameter Norm
    processing temperatures 270 - 310 C -
    Mould temperature 80 - 110 C -
  • product-technical-detail-collapse-item-4-lvl-1
    Predrying Value Unit Parameter Norm
    Permissible residual moisture content 0,1 % -
    Drying temperature 80 - 120 C -
    Drying time 4 - 8 h -