TECAMID 66 GF30 black

PA 66 filled with 30% glass fibres

add to list
product enquiry
request sample
Request machined part
Request customised profile
Request customised tube
PA66 GF30 is a 30 % glass fibre reinforced PA 66. It demonstrates outstanding mechanical properties such as higher strength, rigidity, creep strength and dimensional stability. Compared to unreinforced PA 66, the properties of this glass filled modification GF30 make this material suitable for use in parts that are exposed to high static loads over long periods in high temperature conditions. As glass fibres tend in some cases to have a marked abrasive effect on mating surfaces, Nylon 66 GF30 is less suitable for sliding applications. Due to its black colour additives, black Nylon 66 GF30 shows improved UV protection for outdoor weather resistance applications. Ensinger manufactures PA66 GF30 under the trade name TECAMID 66 GF 30 black.

Compliances

Facts

Chemical designation
PA 66 (Polyamide 66)
Colour
black
Density
1.34 g/cm3

Main Features

  • very high stiffness
  • resistant to many oils, greases and fuels
  • good wear properties
  • very high strength
  • high dimensional stability
  • good weldable and bondable
  • good heat deflection temperature

Target industries

mechanical engineering
aircraft and aerospace technology
automotive industry

Downloads

Datasheet (PDF)
Product handling (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 5500 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 91 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 91 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 8 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 14 % 50mm/min DIN EN ISO 527-2
    Flexural strength 135 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 4700 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 4100 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 25/46/104 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 97 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Shore hardness 86 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 48 C DIN EN ISO 11357
    Melting temperature 254 C DIN EN ISO 11357
    Thermal conductivity 0.39 W/(k*m) ISO 22007-4:2008
    Specific heat 1.2 J/(g*K) ISO 22007-4:2008
    Service temperature 180 C short term -
    Service temperature 110 C long term NN
    Thermal expansion (CLTE) 5 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 5 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1014 Ω Silver electrode, 23°C, 12% r.h. -
    volume resistivity 1014 Ω*cm Silver electrode, 23°C, 12% r.h. -
    Dielectric strength 35 kV/mm 23°C, 50% r.h. ISO 60243-1
    Resistance to tracking (CTI) 550 - 475 V Platin electrode, 23°C, 50% r.h., solvent A DIN EN 60112
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases (+) - -
    Flammability (UL94) HB - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering (+) - NN
    Water absorption 0.1 - 0.2 % 24h / 96h (23°C) DIN EN ISO 62