TECAPEEK SM natural

spin moulded PEEK

add to list
product enquiry
request sample
Request machined part
TECAPEEK SM natural is an unmodified spin moulded Victrex PEEK polymer. One strength of spin moulded material is the flexibility of the wall thickness of up to 30mm, whereas of course there are preferred standard sizes. Rings with outer diameters up to 535mm can be produced. Pipe lengths range between 100 and 500mm.

Facts

Chemical designation
PEEK (Polyetheretherketone)
Colour
beige
Density
1.31 g/cm3

Main Features

  • inherent flame retardant
  • good heat deflection temperature
  • hydrolysis and superheated steam resistant
  • good machinability
  • good slide and wear properties
  • very good chemical resistance

Target industries

oil and gas industry
mechanical engineering
energy industry
chemical technology

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 4300 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 112 MPa 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 14 % 50 mm/min DIN EN ISO 527-2
    Flexural strength 159 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 4200 MPa 2mm/min, 10 N DIN EN ISO 178
    Notched impact strength (Charpy) 6 kJ/m2 DIN EN ISO 179-1eA
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 150 C DIN EN ISO 11357
    Melting temperature 341 C DIN EN ISO 11357
    Service temperature 300 C short term -
    Service temperature 260 C long term -
    Thermal expansion (CLTE) 5 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 6 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 6 10-5*1/K 100-150°C, long. DIN EN ISO 11359-1;2

Stock program