TECAFLON PVDF RP natural

Reprocessed PVDF

add to list
product enquiry
request sample
Request machined part

TECAFLON PVDF RP natural is the environmentally friendly alternative to our conventional material TECAFLON PVDF natural. TECAFLON PVDF RP natural consists of reprocessed PVDF polyvinylidene fluoride and thus offers an optimised CO₂ footprint compared to the fossil-based variant. This does not involve conventional recycling, but rather the reprocessing of PVDF by-products that come from returns through the Ensinger Shapes return program.

TECAFLON PVDF RP natural is comparable in its properties to the fossil-based version and stands out with its high density, strength, and excellent chemical resistance. Additionally, it offers very low moisture absorption and high resistance to UV radiation. These properties make it ideal for demanding applications in various industries where stability and reliability under harsh conditions are required.

Ensinger produces TECAFLON PVDF RP natural stock shapes in the form of plates, rods and PVDF tubes made from reprocessed polyvinylidene fluoride. The PVDF plastic material is part of Ensinger's "Reuse for Tomorrow" solutions and contributes to environmental protection through its reduced CO₂ footprint.

Facts

Chemical designation
PVDF (Polyvinylidene fluoride)
Colour
white
Density
1.78 g/cm3

Main Features

  • from reprocessed by-products/ production residues with optimized PCF
  • very good chemical resistance
  • good slide and wear properties
  • very good weldable
  • very good UV and weather resistance
  • inherent flame retardant
  • very good electrical insulation
  • continuous service temperature up to 150 °C

Target industries

chemical technology
electronics
energy industry
food technology
mechanical engineering

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 2200 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 62 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 62 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 8 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 17 % 50mm/min DIN EN ISO 527-2
    Flexural strength 77 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 2100 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 1900 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 16/28/59 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 150 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) kJ/m2 max. 7,5J DIN EN ISO 179-1eA
    Shore hardness 80 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature -40 C DIN EN ISO 11357
    Melting temperature 171 C DIN EN ISO 11357
    Heat distortion temperature C HDT, Method A ISO-R 75 Method A
    Thermal conductivity 0.25 W/(k*m) ISO 22007-4:2008
    Specific heat 1.3 J/(g*K) ISO 22007-4:2008
    Service temperature 150 C short term NN
    Service temperature 140 C long term -
    Thermal expansion (CLTE) 16 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 18 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1014 Ω -
    volume resistivity O*cm DIN IEC 60093
    Dielectric strength kV/mm DIN 53483-1
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases + -
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering + -
    Water absorption <0.01 % 24h / 96h (23°C) DIN EN ISO 62
    Water absorption % saturation (23°C) DIN EN ISO 62