TECASINT 6022 black

Graphite filled Polyimide for Direct Forming

add to list
product enquiry
request sample
Request machined part
TECASINT 6022 black is a further development of the base polymer TECASINT 6012 natural, which has been specially optimised for tribological applications. This graphite-modified grade is also part of Ensinger's 6000 series, which is processed using the direct forming process. The polyimide is characterised on the one hand by improved wear resistance and heat ageing and on the other hand by very good sliding/friction properties. This PI polymer is therefore successfully used as a standard type in tribological applications in both lubricated and non-lubricated environments. Due to the extreme thermal resistance as well as high creep and wear resistance of this PI polymer, sliding bushings, bearings and seals still function at temperatures, pressures and speeds at which other plastics fail.

Facts

Chemical designation
PI (Polyimide)
Colour
black
Alternative colours available
black
Density
1.47 g/cm3

Main Features

  • very good slide and wear properties
  • good wear resistance
  • very high thermal and oxidative resistance
  • high thermal and mechanical capacity
  • high creep resistance
  • low thermal expansion
  • resistance against high energy radiation
  • sensitive to hydrolysis in higher thermal range

Target industries

mechanical engineering
aircraft and aerospace technology
cryogenic engineering
vacuum technology
automotive industry

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Shore hardness 86 Shore D DIN EN ISO 868
    Impact strength (Charpy) 75.8 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Notched impact strength (Charpy) 5 kJ/m2 max 7.5 J DIN EN ISO 179-1eA
    Tensile strength 65 MPa 50 mm/min DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)    		 5000 MPa 1 mm/min DIN EN ISO 527-1
    Flexural strength 100 MPa 10 mm/min DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 5000 MPa 2 mm/min DIN EN ISO 178
    Compression modulus 2150 MPa 1 mm/min EN ISO 604
    Compressive strain at break 30 % 10 mm/min EN ISO 604
    Elongation at break (tensile test) 1,7 % 50 mm/min DIN EN ISO 527-1
    Compression strength 210 MPa 10 mm/min EN ISO 604
    Elongation at break (flexural test) 2,1 % 10 mm/min DIN EN ISO 178
    Compression strength 155 MPa 10mm/min, 10% strain EN ISO 604
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Thermal conductivity 0,51 W/(k*m) 40°C ISO 8302
    Specific heat 1,12 J/(g*K) -
    Glass transition temperature 283 C -
    Thermal expansion (CLTE) 2.4 - - 10-5*1/K 50-200°C DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 4.4 - - 10-5*1/K 200-300°C DIN EN ISO 11359-1;2
    Service temperature C long term -
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Parameter Norm
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    HZ-Catalogue yes - -
    HZ Technical guidelines yes lbs/in^2 -
    Water absorption 0,3 % 24 h in water, 23°C DIN EN ISO 62
    Water absorption 3.8 % 24 h in water, 80°C DIN EN ISO 62