TECANYL VH2 black

PPE plastic for Aircraft Interiors

add to list
product enquiry
request sample
Request machined part
TECANYL VH2 black is a specially formulated PPE plastic (Polyphenylene ether) designed for use in commercial aircraft interior design. This PPE has been tested to and passed the requirements for FAR 25.853 for aircraft interior materials, as well as specific customer specifications for aircraft interior cabin plastic products. The material's favorable flame and smoke generation characteristics demonstrated in independent flammability tests, make it suitable for applications in aircraft interior spaces such as the galley, bathrooms, and interior cabin space, and even in the flight deck itself. Also available in grey as a custom run item.

Compliances

Facts

Chemical designation
PPE (Polyphenylene ether)
Colour
black
Alternative colours available
grey
Density
1.1 g/cm3

Main Features

  • flame retardant as per FAR 25.853
  • excellent dimensional stability
  • very good chemical resistance
  • flame retardant according to UL94 V-0
  • low smoke emissions
  • low moisture absorption
  • good electrically insulating

Target industries

aircraft and aerospace interiors
aircraft and aerospace technology
Railway Interiors
transportation

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 2300 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 57 MPa 50 mm/min DIN EN ISO 527-2
    Tensile strength at yield 57 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 11 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 20 % 50mm/min DIN EN ISO 527-2
    Flexural strength 96 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 2100 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 1300 MPa 5mm/min EN ISO 604
    Compression strength 19/34/77 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 91 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) 16 % max. 7,5J DIN EN ISO 179-1eA
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 152 C DIN EN ISO 11357
    Service temperature 85 C long term -
    Service temperature 110 C short term -
    Thermal expansion (CLTE) 8,1 10-5*1/K 23-60°C, longitudinal DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 8,1 10-5*1/K 23-100°C, longitudinal DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Parameter Norm
    Flammability (UL94) V0 - -
    Flammability 1.0 mm Glow Wire Flammability Index 960°C passes @ -
    Flammability 775 C Glow Wire Ignitability Temp, 1.0 mm -
    Flammability 775 C Glow Wire Ignitability Temp, 1.5 mm -
    Flammability 775 C Glow Wire Ignitability Temp, 2.0 mm -
    Flammability 800 C Glow Wire Ignitability Temp, 3.0 mm -
    Flammability + - 60 sec. Vertical Bunsen Burner test FAR 25.853 Appx F, Prt 1, (a), 1, (Air) FAR 25.853
    Flammability + - FAR 25.853 Appx F, Prt 1, (a), 1, (Air) FAR 25.853
    Flammability + - FAR 25.853 Appx F, Prt 1, (a), 1, (Air) -
    Flammability ~15 - ASTM E 162 (rail) -
    Flammability 11-13 - ASTM E 662 (Air/Rail) -
    Flammability 20-40 - ASTM E 662 (Air/Rail) -
    Water absorption 0.08/0.15 % 24h / 96h (23°C) DIN EN ISO 62

Stock program