TECAFIL PEEK VX black - 1.75 mm

PEEK FILAMENT BLACK

TECAFIL PEEK VX black is a PEEK filament based on Victrex® PEEK.
It belongs to the PAEK (polyaryletherketone) family, as the base polymer is PEEK (polyetheretherketone) and thus has similar technical properties as the unfilled TECAFIL PEEK VX natural. TECAFIL PEEK VX black is a black pigmented version of PEEK filament for 3D printing. The standard PEEK filaments are usually beige in color. Black PEEK filament is often used for outdoor applications because it has better UV resistance compared to unfilled PEEK.

The base polymer of this filament meets the requirements for food contact according to (EC) No 1935/2004, (EU) No 10/2011, (EC) No 2023/2006 and FDA. Migration tests according to EU 10/2011 were successfully performed on similar extruded specimens. Legally binding documents must be requested separately.

VICTREX® PEEK is a registered trademark of Victrex plc.

Compliances

Facts

Chemical designation
PEEK (Polyetheretherketone)
Colour
black
Density
1.3 g/cm3 (*2)

Main Features

  • inherent flame retardant
  • very good chemical resistance
  • good slide and wear properties
  • good heat deflection temperature
  • resistance against high energy radiation
  • hydrolysis and superheated steam resistant

Target industries

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    General material information Value Unit Parameter Norm
    Diameter 1,75 +/- 0,05 mm -
    Spool measurements Ø 52 mm holder -
    Spool measurements 55 mm width -
    Spool measurements Ø 200 mm outer diameter -
    Spool Material Polycarbonate - -
    Filament Load per Spool 500 g -
  • product-technical-detail-collapse-item-1-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 84,4 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Tensile strength 94,8 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Tensile strength 85,6 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)
    3365,0 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)
    3950,0 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)
    3700,8 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Elongation at break (tensile test) 29,9 % 5mm/min, Orientation XY DIN EN ISO 527-2
    Elongation at break (tensile test) 17,7 % 5mm/min, Orientation XZ DIN EN ISO 527-2
    Elongation at break (tensile test) 5,0 % 5mm/min, Orientation ZX DIN EN ISO 527-2
  • product-technical-detail-collapse-item-2-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 143 C ASTM D 3418
    Melting temperature 343 C DIN EN ISO 11357
    Deflection temperature 162 C HDT-A ISO-R 75 Method A
    Service temperature 300 C short term -
    Service temperature 260 C long term -
    Thermal expansion (CLTE) 5 10-5*1/K DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Moisture absorption 0,03 % DIN EN ISO 62
    Melt flow index (MFI) 8 g/10 min 380°C / 5kg DIN EN ISO 1133
  • product-technical-detail-collapse-item-4-lvl-1
    Processing parameter Value Unit Parameter Norm
    Nozzle temperature 420 - 440 C -
    Max. melt temperature 470 C -
    Print bed temperature 160 - 250 C -
    Build chamber temperature 160 - 230 C -
    Nozzle diameter 0,4 mm -
    Print speed 20 - 30 mm/s -
    Fan speed 0 % -
  • product-technical-detail-collapse-item-5-lvl-1
    Predrying Value Unit Parameter Norm
    Drying temperature 120 C -
    Drying time 8 h -