TECAPAI CM XP530 black-green

Glass Fiber filled PAI

add to list
product enquiry
TECAPAI CM XP530 is a compression moulded polyamide-imide material that is modified with 30% glass fibre filler. Produced using Solvay Torlon® plastic polymer, TECAPAI CM XP530 delivers a unique combination of properties and may be recognized as products commonly referred to in web searches as "torlon 5530". Machining Torlon requires experience. One of the distinctive characteristics of this glass filled PAI is improved machinability when compared to other PAI compression moulded materials. Micro machining with fewer burs left behind than competitive materials is possible. TECAPAI CM XP530 has high strength and stiffness at elevated temperatures, a low CLTE, good dielectric properties, and excellent compressive strength, in addition to excellent chemical resistance.
Typical applications include test sockets in the semiconductor industry, as well as electrical connectors and insulators. Users in aerospace might be interested in this versatile PAI plastic for fasteners and housings, or for other structural components. Minimum order quantities as low as 1 piece adds to the versatility of this PAI product.

Torlon® PAI is a registered trademark of the Solvay Group. 

Facts

Chemical designation
PAI (Polyamide-imide)
Colour
black-green
Density
1.62 g/cm3

Main Features

  • electrically insulating
  • excellent strength and stiffness
  • excellent dimensional stability
  • very good thermal stability
  • excellent chemical resistance

Target industries

semiconductor technology
aircraft and aerospace technology
oil and gas industry
chemical and refinery industry
process engineering

Downloads

Datasheet (PDF)
Product handling (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 5950 MPa 1mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 3,6 % 5mm/min DIN EN ISO 527-2
    Flexural strength 174 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 5900 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression strength 19/43/117 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 40 kJ/m2 max. 7,5J DIN EN ISO 179-1
    Shore hardness 87 - D scale DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 284 C DIN EN ISO 11357
    Thermal expansion (CLTE) 3,1 10-5*1/K 23-60°C, longitudinal DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 3,2 10-5*1/K 23-100°C, longitudinal DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 3,5 10-5*1/K 100-150°C, longitudinal DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    Dielectric strength 32 kV/mm ISO 60243-1
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Water absorption 0,12/0,28 % 24h (23°C) DIN EN ISO 62

Stock program