TECASINT 2031 black

Polyimide with 40 % graphite

add to list
product enquiry
request sample
Starting with the base polymer TECASINT 2011, TECASINT 2031 with 40 % graphite has been developed. The plastic has high resistance to thermal ageing and improved self lubrication. This is accompanied by minimised thermal elongation for dimensionally stable components and increased creep strength.

Facts

Chemical designation
PI (Polyimide)
Colour
anthracite
Density
1.59 g/cm3

Main Features

  • very high creep resistant
  • very good thermal stability
  • good wear resistance
  • high thermal and mechanical capacity
  • very good slide and wear properties
  • low thermal expansion
  • resistance against high energy radiation
  • sensitive to hydrolysis in higher thermal range

Target industries

automotive industry
aircraft and aerospace technology
cryogenic engineering
conveyor technology
hot glass technology
mechanical engineering
precision engineering

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Notched impact strength (Charpy) 3.3 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Impact strength (Charpy) 14.2 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Shore hardness 82 Shore D DIN EN ISO 868
    Tensile strength 52 MPa 50 mm/min DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)    		 5100 MPa 1 mm/min DIN EN ISO 527-1
    Flexural strength 87 MPa 10 mm/min DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 4800 MPa 2 mm/min DIN EN ISO 178
    Compression modulus 1800 MPa 1 mm/min EN ISO 604
    Compressive strain at break 12.5 % 10 mm/min EN ISO 604
    Elongation at break (tensile test) 1.8 % 50 mm/min DIN EN ISO 527-1
    Compression strength 125 MPa 10 mm/min EN ISO 604
    Elongation at break (flexural test) 2.0 % 10 mm/min DIN EN ISO 178
    Compression strength 120 MPa 10mm/min, 10% strain EN ISO 604
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 355 C -
    Heat distortion temperature 325 C 1.8 MPa DIN 53 461
    Thermal expansion (CLTE) 3.0 10-5*1/K 50-200°C DIN 53 752
    Service temperature 290 C long-term -
    Thermal expansion (CLTE) 3.8 10-5*1/K 200-300°C DIN 53 752
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Parameter Norm
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    Water absorption 1.2 % 24 h in water, 23°C DIN EN ISO 62
    Water absorption 2.2 % 24 h in water, 80°C DIN EN ISO 62

Stock program