TECAMID 66 natural

PA 66 unfilled

add to list
product enquiry
request sample
Request machined part
Request customised tube
Request customised profile
Polyamide 66 has good rigidity, hardness, abrasion resistance and thermal dimensional stability. In addition, nylon 66 has outstanding wear resistance and low frictional properties. It also has very good temperature, chemical, and impact properties. Users should be aware of PA 66 propensity to absorb moisture which could affect dimensional stability. In fact, PA 66 will tend to absorb more moisture at saturation than cast PA type 6. It has been successfully used in diverse applications ranging from electronics, marine, and automotive industries, to forrestry, construction and mining.

Compliances

Facts

Chemical designation
PA 66 (Polyamide 66)
Colour
ivory
Density
1.15 g/cm3

Main Features

  • good slide and wear properties
  • electrically insulating
  • good wear properties
  • good weldable and bondable
  • high strength
  • resistant to many oils, greases and fuels
  • high toughness

Target industries

mechanical engineering
food technology
electronics
aircraft and aerospace technology
automotive industry

Downloads

Datasheet (PDF)
Product handling (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 3500 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 85 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 84 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 7 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 70 % 50mm/min DIN EN ISO 527-2
    Flexural strength 110 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 3100 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 2700 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 20/35/81 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) n.b. kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) 5 kJ/m2 max. 7,5J DIN EN ISO 179-1eA
    Shore hardness 82 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 47 C DIN EN ISO 11357
    Melting temperature 258 C DIN EN ISO 11357
    Thermal conductivity 0.36 W/(k*m) ISO 22007-4:2008
    Specific heat 1.5 J/(g*K) ISO 22007-4:2008
    Service temperature 170 C short term NN
    Service temperature 100 C long term NN
    Thermal expansion (CLTE) 11 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 12 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1014 Ω -
    volume resistivity 1014 Ω -
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases (+) - -
    Flammability (UL94) HB - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering - - -
    Water absorption 0.2 - 0.4 % 24h / 96h (23°C) DIN EN ISO 62