TECASON P MT XRO black

X-Ray opaque biocompatible PPSU black

TECASON P MT XRO black is a specifically developed, x-ray detectable biocompatible PPSU plastic (Polyphenylsulfone). With this product line, we meet the challenging demands of minimally invasive and image-controlled surgery. A contrast agent added to the standard product line of medical PPSU material enables x-ray opaque properties and permits clear visibility of components under fluoroscopy and x-ray radiation. It allows the surgeon a precise picture of their medical devices or of orthopaedic trial implants during image-controlled procedures.
PPSU medical grade plastic has improved performance in terms of temperature, impact strength, chemical resistance, and shows exceptional resistance to repeated steam autoclaving without loss of dimensional stability, or physical properties. TECASON P MT XRO has been tested in line with the requirements of ISO 10993 for medical products coming into contact with bodily fluids, bone substance or dentin for up to 24 hours. USP Class VI information is available for raw material. This product line is available in various colours.

Compliances

Facts

Chemical designation
PPSU (Polyphenylsulfone)
Colour
black
Alternative colours available
yellow blue green red grey
Density
1.34 g/cm3

Main Features

  • x-ray opaque
  • high thermal and mechanical capacity
  • hydrolysis and superheated steam resistant
  • good impact strength
  • high stiffness
  • high strength
  • good chemical resistance
  • high gamma radiation resistance

Target industries

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)
    2600 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 77 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 77 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 6 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 50 % 50mm/min DIN EN ISO 527-2
    Flexural strength 107 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    2400 MPa 2mm/min, 10 N DIN EN ISO 178
    Impact strength (Charpy) n.b. kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) 7 kJ/m2 max. 7,5J DIN EN ISO 179-1eA
    Shore hardness 85 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 218 C DIN EN ISO 11357
    Heat distortion temperature C HDT, Method A ISO-R 75 Method A
    Service temperature 190 C short term NN
    Service temperature 170 C long term NN
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases + - -
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering - - -
    Water absorption 0.1 - 0.2 % 24h / 96h (23°C) DIN EN ISO 62
    Water absorption % saturation (23°C) DIN EN ISO 62
  • product-technical-detail-collapse-item-3-lvl-1
    Relative costs Value Unit Parameter Norm
    Relative costs EU from € to €€€€€€ ��� % -