TECAFIL PA6 GF30 black - 1.75 mm

PA6 GF30 Filament

add to list
product enquiry
request sample

In addition to TECAFIL PA6 GF30 black 2,85 mm, we also offer the filament with 1,75 mm diameter. All material characteristics are identical to TECAFIL PA6 GF30 black 2,85 mm. This nylon filament is perfect for all types of industrial 3D printers - even with building chamber temperatures below 80 °C - or desktop printers that can process 1,75 mm filaments.

Facts

Chemical designation
PA 6 (Polyamide 6)
Colour
black
Density
1.36 g/cm3 (*2)

Main Features

  • high strength
  • high dimensional stability
  • good weldable and bondable
  • good heat deflection temperature
  • resistant to many oils, greases and fuels

Target industries

electronics
automotive industry
mechanical engineering

Downloads

Datasheet (PDF)
Product handling (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    General material information Value Unit Parameter Norm
    Diameter 1,75 +/- 0,05 mm -
    Spool measurements Ø 52 mm holder -
    Spool measurements 55 mm width -
    Spool measurements Ø 200 mm outer diameter -
    Spool Material Polycarbonate - -
    Filament Load per Spool 750 g -
  • product-technical-detail-collapse-item-1-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 71,7 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Tensile strength 84,1 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Tensile strength 22,3 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 5215,0 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 6114,0 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 1435,8 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Elongation at break (tensile test) 5,0 % 5mm/min, Orientation XY DIN EN ISO 527-2
    Elongation at break (tensile test) 4,0 % 5mm/min, Orientation XZ DIN EN ISO 527-2
    Elongation at break (tensile test) 3,3 % 5mm/min, Orientation ZX DIN EN ISO 527-2
    Flexural strength 115,0 MPa 2mm/min, Orientation XY DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 4460,0 MPa 2mm/min, Orientation XY DIN EN ISO 178
  • product-technical-detail-collapse-item-2-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 60 C ASTM D 3418
    Melting temperature 220 C DIN EN ISO 11357
    Deflection temperature 200 C HDT-A ISO-R 75 Method A
    Service temperature 180 C short term -
    Service temperature 100 C long term -
    Thermal expansion (CLTE) 6 10-5*1/K DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Moisture absorption 0,3 % DIN EN ISO 62
    Melt flow index (MFI) - g/10 min DIN EN ISO 1133
  • product-technical-detail-collapse-item-4-lvl-1
    Processing parameter Value Unit Parameter Norm
    Nozzle temperature 260 - 290 C -
    Max. melt temperature 300 C -
    Print bed temperature 80 - 140 C -
    Build chamber temperature 80 - 100 C -
    Nozzle diameter 0,4 - 0,6 mm -
    Print speed 30 - 50 mm/s -
    Fan speed 0 % -
  • product-technical-detail-collapse-item-5-lvl-1
    Predrying Value Unit Parameter Norm
    Drying temperature 80 C -
    Drying time 8 h -