TECACOMP PA66 CF30 black 1014809

Polyamide 66 compound with 30 % carbon fibers

The semi-crystalline thermoplastic nylon 66 enables numerous applications. The use of 30 % carbon fibers improves mechanical strength at low density, increases the modulus of elasticity and provides excellent tensile strength. 

The carbon content also improves heat resistance. TECACOMP PA66 CF30 black can be used up to 110 °C permanently and up to 170 °C for short periods, for example in the automotive industry, mechanical engineering, office machines or precision engineering.

Facts

Chemical designation
PA 66 (Polyamide 66)
Colour
black
Density
1.27 g/cm3

Main Features

  • very high stiffness
  • high strength
  • good wear properties
  • good heat deflection temperature
  • resistant to many oils, greases and fuels
  • good weldable and bondable
  • low viscosity

Target industries

Downloads

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 267 MPa DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)
    21000 MPa DIN EN ISO 527-1
    Elongation at break (tensile test) 2,0 % DIN EN ISO 527-1
    Impact strength (Charpy) 54 kJ/m2 DIN EN ISO 179-1eU
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 5 - 72 C -
    Melting temperature 260 C -
    Heat distortion temperature 259 C ISO-R 75 Method A
    Service temperature 170 C short term -
    Service temperature 110 C long term -
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 103 DIN EN 61340-2-3
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Molding shrinkage 0,2 % longitudinal DIN EN ISO 294-4
    Molding shrinkage 0,7 % transverse DIN EN ISO 294-4
  • product-technical-detail-collapse-item-4-lvl-1
    Processing parameter Value Unit Parameter Norm
    processing temperatures 270 - 310 C -
    Mould temperature 80 - 110 C -
  • product-technical-detail-collapse-item-5-lvl-1
    Predrying Value Unit Parameter Norm
    Permissible residual moisture content 0,1 % -
    Drying temperature 80 - 120 C -
    Drying time 4 - 8 h -