TECASINT 5111 natural

unfilled polyimide

add to list
product enquiry
request sample
Request machined part
The unfilled grade TECASINT 5111 natural is based on the high-performance plastic polyimide, which is characterised by its very good thermal stability with low thermal expansion. Polyimides are non-melting polymers with a service temperature of 300 °C, which is considerably higher than that of PEEK or PPS. In addition, TECASINT 5111 natural has a high creep resistance. These properties makes PI plastic ideal for applications where high temperature resistance is required, such as in the aerospace industry.

TECASINT 5111 natural has good chemical resistance, especially to light acids and many organic solvents.
In combination with the very good electrical insulating properties of the PI material, TECASINT 5111 natural is also perfectly suited for applications in the semiconductor industry, electrical engineering or mechanical engineering.

Moreover, the polyimide material has good mechanical properties, good wear resistance and is also resistant to high-energy radiation.

TECASINT 5111 natural is produced as polyimide sheet, polyimide rod and tube.

Facts

Chemical designation
PI (Polyimide)
Colour
black
Density
1.33 g/cm3

Main Features

  • very good electrical insulation
  • high thermal and mechanical capacity
  • good wear resistance
  • high creep resistance
  • resistance against high energy radiation
  • sensitive to hydrolysis in higher thermal range

Target industries

semiconductor technology
electrical engineering
aircraft and aerospace technology
cryogenic engineering
mechanical engineering
nuclear and vacuum technology

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Impact strength (Charpy) 70 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Shore hardness 91 Shore D DIN EN ISO 868
    Tensile strength 140 MPa 50 mm/min DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)    		 3800 MPa 1 mm/min DIN EN ISO 527-1
    Flexural strength 205 MPa 10 mm/min DIN EN ISO 178
    Compression strength 440 MPa 10 mm/min EN ISO 604
    Compressive strain at break 48 % 10 mm/min EN ISO 604
    Elongation at break (tensile test) 5.3 % 50 mm/min DIN EN ISO 527-1
    Modulus of elasticity
    (flexural test)    		 3600 MPa 2 mm/min DIN EN ISO 178
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 330 C -
    Thermal expansion (CLTE) 4.6 - - 10-5*1/K 50-200 °C DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 4.5 - - 10-5*1/K 100-150 °C DIN EN ISO 11359-1;2
    Specific heat 1.116 J/(g*K) DIN EN 821
    Thermal conductivity 0.215 W/(k*m) DIN EN 821
    Heat distortion temperature 335 C 1,8 MPa DIN 53 461
    Thermal expansion (CLTE) 4.1 - - 10-5*1/K 23-100°C DIN EN ISO 11359-1;2
    Service temperature 300 C short-term -
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1015 Ω 23°C DIN IEC 60093
    volume resistivity 1014 Ω*cm 23°C DIN IEC 60093
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    Water absorption 0.82 % 24 h in water, 23°C DIN EN ISO 62
    Water absorption 2.24 % 24 h in water, 80°C DIN EN ISO 62