TECAMID 66 GF15 FR black

Flame retardant pa 66 glass filled for aircraft

add to list
product enquiry
request sample
Request machined part
TECAMID 66 GF15 FR black is a specially formulated glass filled 66 nylon plastic designed for use in aircraft design when additional stiffness and strength might be required in a given aircraft aerospace material application. This PA66 plastic has been tested to and passed the requirements for FAR 25.853 for aircraft interior materials, and could be considered as a more cost effective option than some other higher performance materials such as PEEK or PPS. The fiber reinforced material's favorable flame and smoke generation characteristics demonstrated in independent flammability tests make it suitable for structural support applications in aircraft interior spaces.

Compliances

Facts

Chemical designation
PA 66 (Polyamide 66)
Colour
black
Density
1.31 g/cm3

Main Features

  • flame retardant as per FAR 25.853
  • low smoke emissions
  • resistant to many oils, greases and fuels
  • high strength
  • good mechanical properties

Target industries

aircraft and aerospace interiors
aircraft and aerospace technology
mechanical engineering
transportation

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 3700 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 54 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 54 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 7 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 7 % 50mm/min DIN EN ISO 527-2
    Flexural strength 103 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 3500 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 1600 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 23/42/90 % 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 40 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Impact strength (Charpy) 4 kJ/m2 max. 7,5J DIN EN ISO 179-1eA
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Melting temperature 261 C DIN EN ISO 11357
    Service temperature 110 C long term -
    Service temperature 180 C short term -
    Thermal expansion (CLTE) 5 10-5*1/K 23-60°C, longitudinal DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 5 10-5*1/K 23-100°C, longitudinal DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Parameter Norm
    Flammability pass - 60 seconds Vertical Bunsen Burner test AITM 2.0002A
    Flammability pass - 15 seconds HorizontalBunsen Burner test AITM 2.0003
    Flammability pass - Specific Optical Smoke Density AITM 2.0007B
    Flammability pass - 60 seconds Vertical Bunsen Burner test 25.853 (a) Amdt 25-116 App F Part 1(a)(1)(i) FAR 25.853
    Flammability pass - Gas Toxicity, as Per Airbus directive ABD0031 AITM 3.0005
    Water absorption 0.36/0.76 % 24h / 96h (23°C) DIN EN ISO 62